Designation by Standards
| Brand Name |
Ravne No. |
Mat. No. |
DIN |
EN |
AISI |
| MERILO |
802 |
1.2842 |
90MnCrV8 |
90MnV8 |
O2 |
Chemical Composition (in weight %)
| C |
Si |
Mn |
Cr |
Mo |
Ni |
V |
W |
Others |
| 0.90 |
0.25 |
2.00 |
0.35 |
- |
- |
0.13 |
- |
- |
Description
Cold work tool steel with high dimensional stability at heat treatment. Very high resistance to cracking. High machinability, medium thoughness and resistance to wear.
Applications
Measuring tools, machine knives for the wood, paper and metal industry, cold cutting shear blades, thread cutting tools.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [10
3 x N/mm
2]: 210
Density [g/cm
3]: 7.85
Thermal conductivity [W/m.K]: 30.0
Electric resistivity [Ohm mm
2/m]: 0.35
Specific heat capacity[J/g.K]: 0.46
Coefficient of Linear Thermal Expansion 10-6 oC-1
| 20-100oC |
20-200oC |
20-300oC |
20-400oC |
20-500oC |
20-600oC |
20-700oC |
| 12.1 |
13.3 |
13.8 |
14.3 |
14.1 |
14.2 |
14.6 |
Continuous Cooling Transformation (CCT) Diagram
Click the image to enlarge the diagram.
Time-Temperature Transformation (TTT) Diagram
Click the image to enlarge the diagram.
Soft Annealing
Heat to 690-720
oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 229.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to
650
oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 790-820
oC followed by oil or warm bath
(180-220
oC) quenching. Hardness after quenching is 63-65 HRC.
Tempering
Tempering temperature: See the data bellow.
Tempering Temperature (oC) vs. Hardness (HRC)
| 100oC |
200oC |
300oC |
400oC |
500oC |
600oC |
| 63 |
60 |
56 |
50 |
42 |
38 |
Tempering Diagram
Click the image to enlarge the diagram.
Forging
Hot forming temperature: 1050-850
oC.
Machinability
No data.
Corrosion Resistance
Corrosion resistance of this alloy is better than that of plain carbon steels. However it will rust unless given protective treatment.
Forms manufactured: Please see the
Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
Unless otherwise specified, registered trademarks are property of Metal Ravne company. Copyright 2011 by Metal Ravne. All rights reserved.
Contact our
Sales Office for more information.